TITAN CR681

CR681 is a rutile titanium dioxide produced by the chloride process with surface treatment of Al2O3, ZrO2 and special organic compounds. It allows to obtain high-gloss coatings, is easily dissolved and dispersed, has high hiding power and durability. It is recommended for use in solvent-based coatings, bright paints for external use, smooth emulsion paints for internal use, industrial coatings, printing inks and plastics.

Technical characteristics

• Inorganic compound for surface treatment - Al2O3, ZrO2
• Organic compound for surface treatment - Yes
• TiO2 content, % (mass fraction) - ≤92
• Rutile content, % - ≤99
• Tint reduction, relative lightening - ≤1950
• Oil absorption, % (mass fraction) - ≥20
• pH factor of aqueous suspension - 6.5- 8.0
• Electrical resistance of aqueous solution, Ωm - –
• Volatility at 105 C, % (g/100g) - –
• Solubility in water, % - –
• Sieve residue (45 mesh ≤ μm), % (mass fraction) - –
• Brightness - ≥98
• Specific density - 4.1
• Average particle size - 0.23

Manufacturer

TITANOS - China

Storage conditions

At any temperature. Guaranteed shelf life - 12 months

Packaging

bags - 25 kg.